Ambica Steels specializes into the production of 17-4 steels (also known as 1.4542 Bar and AISI 630). This is a precipitation hardening martensitic stainless steel with Cu and Nb/Cb additions. The grade combines a very high strength, hardness (up to 572°F / 300°C), and corrosion resistance.

Mechanical properties can be optimized with various heat treatments. Very high yield strength up to 1100-1300 MPa (160-190 ksi) can be achieved. Ambica Steels offers various heat treatments in this grade like – Solution Annealed, H900, H925, H1025, H1075, H1150, H1150D, H1150M, P800, P930, P960, P1070 etc with both Air & Oil quenching,

Ambica Steels produces all materials in this grade – Bright Round Bars, PSQ / BSQ Bars, HRAP Squares / Hexagons, HRAP Flat Bars, HR Bars & RCS, Concast Billets, Ingots.

Ambica ist spezialisiert auf die Produktion von 17-4 Edelstahl (auch bekannt unter 1.4542 und AISI 630). Das ist ein aushärtbarer, martentistischer Edelstahl mit Cu und Nb/Cb Zusätzen. Die Sorte kombinierte eine sehr hohe Stärke und Härte (bis 572°F / 300°C) mit hoher Korrosionsresistenz.

Die mechanischen Eigenschaften können durch verschiedene Wärmebehandlungen optimiert werden. So kann eine extrem hohe Streckgrenze bis 1100-1300 MPa (160-190 ksi) erreicht werden. AMBICA bietet für diese Sorte eine Reihe von Wärmebehandlungen, wie – Lösungsgeglüht, H900, H925, H1025, H1075, H1150, H1150D, H1150M, P800, P930, P960, P1070 etc. Luft & Ölabschreckung.

Ambica produziert alle Materialien in dieser Sorte – Blanke Rundstäbe, PSQ / BSQ Stäbe, HRAP Vierkant / Sechskant, HRAP Flachstahl, HR Stäbe & RCS, gegossene Knüppel, Rohblöcke.

Specifications of 17-4 ph Stainless Steel Spezifikationen

AMS 5643R, DIN/EN 10088-3, AMS 5622, ASTM A564 AMS 5643R, DIN/EN 10088-3, AMS 5622, ASTM A564

Benefits Offered Enthaltene Vorteile
  • High tensile strength and toughness Hohe Zugfestigkeit und Zähheit
  • High hardness up to 41 HRC Hohe Härte bis 41 HRC
  • Excellent corrosion resistance Exzellenter Korrosionswiderstand
  • Suitable for forging and welding Geeignet zum Schmieden und Schweißen
  • Good machinabilty Gute maschinelle Bearbeitbarkeit
  • Good oxidation resistance Guter Oxidationswiderstand
  • Close hardness range of 29-33 HRC Enge Härtebereich von 29-33 HRC
  • Good resistance to sulphide stress cracking Widerstandsfähig gegen Sulfid-Spannungsrisse
Applications/Usage Applikationen/Verwendung
  • Oil and gas industry
  • Pumps and valves in high pressure components Öl und Gasindustrie
  • Chemical process equipment Pumpen und Ventile bei Hochdruckkomponenten
  • Measuring and control techniques Messungs- und Kontrollwerkzeuge
  • Food industry Lebensmittelindustrie
  • Aerospace Luftfahrt
  • Pulp and paper industry Zellstoff- und Papierindustrie
  • Mechanical components Mechanische Komponenten
  • Power generation Kraftwerke
  • Nuclear reactor components Komponenten für Atomreaktoren

There are a multitude of cast and wrought stainless steel alloys that can have various desirable characteristics enhanced by either solution treating or by solution treating and precipitation age hardening. Characteristics such as room temperature and/or elevated temperature mechanical strength and corrosion resistance are typically enhanced by such heat treatments.

The properties of precipitation hardenable stainless steels can be enhanced by selection of appropriate heat treating parameters. The use of solution treating alone or solution treating followed by precipitation age hardening is commonly used with precipitation hardenable stainless steels.

Für Schmiede- und Gussstahllegierungen gibt es eine Vielzahl von Möglichkeiten durch Lösungsglühung oder Ausscheidungshärtung gewünschte Charakteristika zu erreichen. Typischerweise werden folgende Charakteristika verbessert: mechanische Stärke bei Raum- oder Extremtemperatur, Korrosionswiderstand. Das erreicht man normalerweise mit Wärmebehandlungen.

Die Eigenschaften von aushärtbarem Stahl können durch die gezielte Auswahl von Wärmebehandlungsparametern verbessert werden. Lösungsglühung alleine, oder Lösungsglühung mit anschließender Ausscheidungshärtung wird normalerweise mit aushärtbaren Edelstahlsorten angewendet.